3 Search Results

We used scanning tunnelling microscopy to study the morphology of an overlayer of ceria in contact with a TiO₂(110) substrate. Two types of domains were observed after ceria deposition. An ordered ceria film covered half of the surface and high-resolution imaging suggested a near-c(6 × 2) relationship to the underlying TiO₂(110)-(1 × 1). For the other half of the surface, it comprised CeO_x nanoparticles and reconstructed TiOx supported on TiO₂(110)-(1 × 1). Exposure to a small amount of gold resulted in the formation of isolated gold atoms and small clusters on the ordered ceria film and TiO₂(110)-(1 × 1) areas,more » which exhibited significant sintering at 500 K and showed strong interaction between the sintered gold clusters and the domain boundaries of the ceria film. The Au/CeO_x/TiO₂(110) model system proved to be a good catalyst for the water–gas shift (WGS) exhibiting much higher turnover frequencies (TOFs) than Cu(111) and Pt(111) benchmarks, or the individual Au/TiO₂(110) and Au/CeO₂(111) systems. Finally, for Au/CeO_x/TiO₂(110) catalysts, there was a decrease in catalytic activity with increasing ceria coverage that correlates with a reduction in the concentration of Ce^{3 +} formed during WGS reaction conditions.« less

Low-coordinated sites are surface defects whose presence can transform a surface of inert or noble metal such as Au into an active catalyst. We prepared gold surfaces modified by pits, starting with a well-ordered Au(111) surface; we then used microscopy (STM) for their structural characterization and CO spectroscopy (IRAS and NEXAFS) for probing reactivity of surface defects. In contrast to the Au(111) surface CO adsorbs readily on the pitted surfaces bonding to low-coordinated sites identified as step atoms forming {111} and {100} microfacets. Finally, pitted nanostructured surfaces can serve as interesting and easily prepared models of catalytic surfaces with definedmore » defects that offer an attractive alternative to vicinal surfaces or nanoparticles commonly employed in catalysis science.« less

Adsorbate-driven morphological changes of pitted-Cu(111) surfaces have been investigated following the adsorption and desorption of CO and H. The morphology of the pitted-Cu(111) surfaces, prepared by Ar⁺ sputtering, exposed a few atomic layers deep nested hexagonal pits of diameters from 8 to 38 nm with steep step bundles. The roughness of pitted-Cu(111) surfaces can be healed by heating to 450-500 K in vacuum. Adsorption of CO on the pitted-Cu(111) surface leads to two infrared peaks at 2089-2090 and 2101-2105 cm^-1 for CO adsorbed on under-coordinated sites in addition to the peak at 2071 cm^-1 for CO adsorbed on atop sitesmore » of the close-packed Cu(111) surface. CO adsorbed on under-coordinated sites is thermally more stable than that of atop Cu(111) sites. Annealing of the CO-covered surface from 100 to 300 K leads to minor changes of the surface morphology. In contrast, annealing of a H covered surface to 300 K creates a smooth Cu(111) surface as deduced from infrared data of adsorbed CO and scanning tunnelling microscopy (STM) imaging. The observation of significant adsorbate-driven morphological changes with H is attributed to its stronger modification of the Cu(111) surface by the formation of a sub-surface hydride with a hexagonal structure, which relaxes into the healed Cu(111) surface upon hydrogen desorption. These morphological changes occur ~150 K below the temperature required for healing of the pitted-Cu(111) surface by annealing in vacuum. In contrast, the adsorption of CO, which only interacts with the top-most Cu layer and desorbs by 160 K, does not significantly change the morphology of the pitted-Cu(111) surface.« less